Abstract
The dynamic and static softening phenomena in Al–6Mg alloy were studied through interrupted two-stage hot compression test performed isothermally at 480°C and strain rate range of 0.001–0.1s−1. The interruptions of 29 and 90s were considered when the true strain reached 0.5. It was concluded that the effect of static softening on the flow stress was not highlighted by extending the interruption at a constant strain rate. Also, it was exhibited that softening rate highly enhanced with the strain rate decrement at a constant time. Moreover, the static and dynamic recrystallization was revealed as the dominant softening mechanisms at low and high strain rates, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.