Abstract
Tin doped zinc oxide (ZnO:Sn) thin films were deposited onto Pyrex glass substrates by chemical spray pyrolysis technique starting from zinc acetate (CH3CO2)2Zn⋅2H2O and tin chloride SnCl2. The effect of Sn doping on structural, optical and electrical properties was investigated. The atomic percentages of dopant in ZnO-based solution were y=[Sn4+]/[Zn2+]=0%, 0.2%, 0.6% and 1%. It was found that all the thin films have a preferential c-axis orientation. With increase of Sn doping, the peak position of the (002) plane was shifted to the high 2θ values. ZnO:Sn demonstrated obviously improved surface roughness, reduced average crystallite size, enhanced Hall mobility and reduced resistivity. Among all of the tin doped zinc oxide in this study, films doped with 0.6at.% Sn concentration exhibited the best properties, namely a Hall mobility of 9.22cm2V−1s−1, an RMS roughness of 37.15nm and a resistivity of 8.32×10−2Ωcm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.