Abstract
Spinel LiNi0.5Mn1.5O4 is a very important and promising cathode material for lithium ion batteries. The strategy of doping elements is a common used way to improve its electrochemical properties. The action mechanism of doping elements in LiNi0.5Mn1.5O4 is complex. In this study, we synthesized the Cr, Fe-doped compounds LiNi0.45M0.1Mn1.45O4 (M=Cr, Fe) and pristine compound LiNi0.5Mn1.5O4 at the same annealing conditions. The as prepared samples display different morphological features. The thermogravimetric analysis shows different situation for these samples. Oxygen dissipation in the Cr-doped compound at high temperature is less than the other two samples. The XPS spectra display that the doping elements have influences on the chemical valence of Ni, and result in more Ni(III) amount in the Cr, Fe-doped products. The doped compounds exhibit excellent rate capability. At 10C-charge/10C-discharge rate, their capacities are 85mAhg−1, 74mAhg−1 and 50mAhg−1 for LiNi0.45Fe0.1Mn1.45O4, LiNi0.45Cr0.1Mn1.45O4 and LiNi0.5Mn1.5O4, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.