Abstract
CuSn6Zn6 alloy powder and a pore former were used as raw material. Porous bronze was successfully prepared by the sintering and dissolution process (SDP). The porosity is in range of 76%~88%, and the pore size is in range of 0.8~3.3mm. The effect of the porosity and cell sizes of specimens on its mechanical property was investigated, and the effect of sintering temperature on its relative density and porosity was also studied. The experimental results indicate that under the condition of the same pore size, the compressive strength decreases with the increase of porosity, the compressive strength changes from 10Mpa to 2Mpa with the porosity from 76% to 88%; under the same porosity condition, the compressive strength does not change significantly with the pore size, but it has a slightly increasing trend with the decrease of the pore size. The relative density of the specimens increases with the increase of the sintering temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.