WC@C nano composite was prepared by a single step solid–state reaction through in situ reduction and carburization of WO3 in the presence of Mg and activated charcoal. The XRD results and thermodynamics analysis showed that the optimization of reaction temperature facilitates the reduction as well as carburization of tungsten oxide(s) at different reaction temperature. Thermogravimetric analysis of the product was done to assess the thermal stability in air. The Raman spectroscopy was used to find out the nature (amorphous/graphitic) of carbon in the obtained phase. The N2 adsorption–desorption measurement showed a narrow pore size distribution from 3 to 4 nm with BET surface area of up to 522.5 m2/g. TEM/HRTEM images confirmed formation of the WC nano particles with spherical morphology. Electrochemical stability of pure and platinized carbide sample (Pt/WC) has been investigated using cyclic voltammetry in acidic media for alcohol (methanol and ethanol) oxidation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.