Study on Physical and Mechanical Properties of Cu/MoS<sub>2</sub> Composites

Abstract

Cu-3wt. %MoS2-7wt. %Mo and Cu-3wt. %MoS2 composites were prepared by repressing, re-sintering and vacuum hot pressing, respectively. Microstructures were characterized by optical metallographic microscope, EDS, SEM and X-ray diffraction analysis, respectively. The micro hardness, electric conductivity and density of samples were separately measured as well. Results show that the micro hardness of Cu-3wt. % MoS2-7wt. % Mo composites is about 33.3% higher than that of Cu-3wt. %MoS2 composites. The increase in micro hardness is attributed to the presence of Mo. The electric conductivity of Cu-3wt. %MoS2 and Cu-3wt. %MoS2-7wt. % Mo prepared by vacuum hot pressing were 80.6 % and 63.8% IACS, respectively, which is an increase compared with values of 80.2 % and 57.3% IACS of samples obtained by repressing and re-sintering.