Abstract
In this paper, a metal inert gas (MIG) shielded welding method was used for high-quality welding of 6063-T6 aluminum alloy sheet with a thickness of 2.5 mm. The welding process of MIG welding was accurately simulated and the welding temperature field and thermal cycle curve were calculated using a combination of Gaussian body heat source and double ellipsoidal heat source. As the welding current increased from 75 A to 90 A, the reinforcing phase precipitated under the microstructure of the joint gradually became larger and re-solidified into the body, resulting in a reduction in mechanical properties. When the welding current is 85 A, the pitting resistance of weld forming and weld area reaches its optimum. At this time, the tensile strength of the joint is up to 110.9 MPa, the elongation is up to 16.3% and the Vickers Microhardness is up to 46.9 HV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.