Abstract
: Strontium hexaferrite (SrFe12O19) materials were synthesized through the hydrothermal method with conditions at R= (Fe3++ Sr2+)/(OH ̶) ratio of 2 to 4 (R ratio of 1/2, 1/3 and 1/4 were, respectively abbreviated to M2, M3 and M4). R has been examined by employing Fe(NO3)3 and Sr(NO3)2 as the initial materials. The effects of R ratio on the structure, particle size, magnetic and microwave-absorbing properties of the samples were studied. The coercivity and saturation magnetization of M4 sample reach 5.2 kOe and 58.7 emu/g, respectively. The optimal reflection loss of the M4 at the thickness of 1.5 mm reached a value as large as - 48.27 dB in the frequency range of 2 to 18 GHz. The improvement in microwave absorption performance of M4 sample compared to M2 and M3 was mainly resulted from the increased magnetic properties with increasing R ratio. 
 
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.