Abstract
The effects of CuSO4 concentration, voltage and treating time on the hemisphere emissivity and corrosion resistance of AZ31B magnesium-alloy black micro-arc oxidation coatings were studied by orthogonal experiment. The microstructure, phase composition, corrosion resistance and hemisphere emissivity of the coating were investigated by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy, electrochemical test and infrared emissivity spectrometer, respectively. The results showed that the influences of each factor on corrosion current density and the hemisphere emissivity are as follows: voltage > treating time > CuSO4 concentration. The black MAO coatings are mainly composed of WO3, MgAl2O4, CuAl2O4, MgO, CuO and MgF2. The CuO and CuAl2O4 phases are the main reasons for blackness of the coatings. The coating exhibits the best corrosion resistance under the conditions of CuSO4 concentration 1.5 g/L, oxidation voltage 500 V and treating time 10 min. Additionally, the variation trends of hemispherical emissivity and roughness of the black MAO coating are the same when the composition of the coatings is similar. When the concentration of CuSO4 is 1.5 g/L, the oxidation voltage is 450 V and the treatment time is 10 min, the coating with the highest hemispherical emissivity of 0.84 can be obtained.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.