Study on Laser Polishing of Ti6Al4V Fabricated by Selective Laser Melting.

Abstract

Laser-based additive manufacturing has garnered significant attention in recent years as a promising 3D-printing method for fabricating metallic components. However, the surface roughness of additive manufactured components has been considered a challenge to achieving high performance. At present, the average surface roughness (Sa) of AM parts can reach high levels, greater than 50 μm, and a maximum distance between the high peaks and the low valleys of more than 300 μm, which requires post machining. Therefore, laser polishing is increasingly being utilized as a method of surface treatment for metal alloys, wherein the rapid remelting and resolidification during the process significantly alter both the surface quality and subsurface material properties. In this paper, the surface roughness, microstructures, microhardness, and wear resistance of the as-received, continuous wave laser polishing (CWLP), and pulsed laser polishing (PLP) processed samples were investigated systematically. The results revealed that the surface roughness (Sa) of the as-received sample was 6.29 μm, which was reduced to 0.94 μm and 0.84 μm by CWLP and PLP processing, respectively. It was also found that a hardened layer, about 200 μm, was produced on the Ti6Al4V alloy surface after laser polishing, which can improve the mechanical properties of the component. The microhardness of the laser-polished samples was increased to about 482 HV with an improvement of about 25.2% compared with the as-received Ti6Al4V alloy. Moreover, the coefficient of friction (COF) was slightly reduced by both CWLP and LPL processing, and the wear rate of the surface layer was improved to 0.790 mm3/(N∙m) and 0.714 mm3/(N∙m), respectively, under dry fraction conditions.