Abstract
Hot compression deformation behavior of TC4 titanium alloy was studied on Thermecmaster-Z simulator in the temperature range 850 degrees C similar to 1150 degrees Cand strain rate range 0.5 s(-1)similar to 30s(-1). The results show that deformation temperature and strain rate both have significant influence on the flow stress. The flow stress decreases with the increase of deformation temperature, while increases with the increase of strain rate. The deformation mechanism of TC4 alloy exhibit dynamic recovery feature in high temperature. However, in lower temperature, dynamic recrystallization and grain boundary slip behavior may take place. Deformation activation energy values are 863.46 kJ/mol in (alpha + beta) phase region, and 209.80 kJ/mol in beta region respectively. Constitutive equations of TC4 alloy described by Zener-Hollomon parameter were formulated. Therefore, a scientific basis is provided for the reasonable choice of thermal parameters of TC4 titanium alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.