Abstract
Warm compacting and sintering behaviors of pre-mixed Fe-2Ni-2Cu-1Mo-1C powders were studied. Results showed that green density increased with compacting temperature and then fell slightly; the maximum green density was obtained at about 120°C. Green compact density and spring back effect of the pre-mixed powder increased gradually as the compacting pressure increased. Sintered density first increased and then fell as the temperatures went up under different sintering temperatures for 50 minutes, but the trends of sintering dilatation were first reduced and then increased. Sintered density first reduced and then increased with the prolonged sintering time at 1300°C, but the trends of dimension change after sintering were the very reverse. Tensile strength, elongation and hardness of the warm compacted Fe-2Ni-2Cu-1Mo-1C materials generally increased as sintering temperature and sintering time went up.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.