Abstract
A new technology, duplex ion nitrocarburizing and sulphurizing technology (DINS), for friction reduction and anti-scuffing applications of diesel engine cylinder was studied. Duplex ion nitrocarburized-sulphurized layer was prepared on the surface of CrMoCu alloy cast iron by using the DINS process. The morphology, phase structure and tribological behaviors under sulphur contained additive lubrication were investigated. Results show that the sulphide surface layer of the duplex layer is mainly composed of close-packed hexagonal structured FeS phase and cubic structured FeS2 phase. The nitrocarburized sub-surface layer of the duplex layer is mainly composed of Fe2C and Fe3N phases. The harder nitrocarburized layer can provide effective support to the softer sulphide layer and avoid its lamellar tear. The synergistic effect between the duplex layer and the sulphur contained additive lubricant, resulted in 10% and 33.3% reduction in coefficient of friction and wear volume, respectively, compared with those of the sulphurized surface, and 25% and 50.1% reduction, respectively, compared with those of the plain surface. Bench test of diesel engine further demonstrated that the DINS process can provide the treated cylinder with superior properties in anti-scuffing and friction reduction, so that it can be used to prolong the service life of the cylinder.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.