Abstract
The effect of specimen size and shape on the fatigue life of reduced activation ferritic/martensitic steel “F82H IEA-heat” was investigated to develop a fatigue life evaluation method using a small specimen for testing neutron-irradiated materials. The fatigue test was carried out at room temperature in air using three kinds of round-bar specimen (minimum diameter cross sections of 1, 4, and 7 mm) and one hourglass specimen (minimum diameter cross section of 1.25 mm). The effect of specimen size on fatigue life from a level of 103 to 104 cycles was almost negligible for the round-bar specimens. The shorter fatigue life at the total strain range below 0.6% and the slightly longer fatigue life at the total strain range above 0.8% of the hourglass specimen relative to that of the standard specimen were observed from a level of 102 to 104 cycles.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.