Abstract
Based on ferro based superalloy K273 and heat resistant steel ZG40Cr24, test alloys were cast by intermediate frequency induction furnace with non-oxidation method by alloying of aluminium and silicon. The oxidation resistance at 1100°C for 500 hours of test alloys was carried out according to oxidation weight gain method. Experimental results show that the scale exfoliation resistance of K273 and ZG40Cr24 is reinforced greatly by Al2O3 and SiO2. The scale exfoliation weight gain rate at 1100°C descends from 1.2681g.m-2.h-1 to zero, reaching complete exfoliation resistance for ZG40Cr24 test alloy. Because of 1.5<PBR(Al2O3⁄Fe)<2 and the growing of Al2O3 and SiO2 from out side of scale-scale/oxygen interface, the composite scale grows intact and compact without accumulation of growing stress.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.