Abstract
Metals play a pivotal role in industry; their use constantly grows. It is virtually impossible to find an industrial field without the use of metals and their alloys. However, owing to the quality degradation of metal during the operational process, corrosion appears not only on its surface but also under a coating, which leads to its destruction. To avoid this, corrosion inhibitors are necessary. Organic compounds have been widely used as corrosion inhibitors. Many organic corrosion inhibitors have been developed nowadays. In the literature, organic compounds comprising N, O, S and P heteroatoms are described, which reduce corrosion rate. The organic compounds are adsorbed on the metal surface, forming a thin layer. Adsorption occurs either through electrostatic interaction or, in some cases, the formation of covalent bonds. The work aimed to study isothiuronic salts as corrosion inhibitors to evaluate their protective properties using the polarisation curves method. Objects of research were isothiuronic compounds containing two active centres separated by saturated and unsaturated carbon bonds (structures 1-3). In structures 4-7, one isothiuronic fragment has different propylene substituting groups. It has been previously shown that these compounds can act as effective brightening agents when applying nickel coatings. A model solution with a density of 1.12 g/cm3 was prepared to study the corrosion inhibitors. The corrosion inhibitor concentration was 400 mg/L. Studies have shown that the compounds with two isothiuronic moieties do not always exhibit improved properties for inhibiting metal degradation in a corrosive environment. In particular, they showed worsening of the inhibiting properties for samples made of steel 20 and identical properties for that made of steel 3.
Highlights
For citation: Ushakov IA, Nikonova VS, Polynskii IV, Knyazeva LG, Polynskaya MM, Antsiferov EA
Study on efficiency of corrosion inhibitors based on derivatives of isothiuronic salts
The final manuscript has been read and approved by all the co-authors
Summary
Объектами исследований выступили изотиуронивые соли (1–7), содержащие два активных центра (1–3), разделенных насыщенными и ненасыщенными углеродными связями. Точное определение этих параметров может быть выполнено путем преобразования уравнения Батлера – Фольмера для диапазона высоких поляризаций к набору экспериментальных данных с учетом того, что ток коррозии связан с поляризационным сопротивлением и наклонами Тафеля:. Для исследованных соединений 1–7 на образцах стали марок Ст20 и Ст3 были получены поляризационные кривые Наклоны Тафеля на анодных кривых близки для разных ингибиторов коррозии на сталях Ст3 и Ст20, следовательно, ионизация железа протекает по одному механизму:. Экспериментальные значения тока и потенциала коррозии для ингибиторов 1–7. Наибольший защитный эффект ингибиторов коррозии проявляется на стали Ст3, на стали Ст20 ингибиторы 1 и 3 являются стимуляторами коррозионных процессов. Определено, что все исследованные соединения относятся к классу ингибиторов поверхностно-активного типа, так как тормозят процесс коррозии за счет адсорбции. Ингибиторы коррозии, имеющие два изотиуроневых фрагмента, не всегда показывают улучшение свойств для ингибирования металла в коррозионной среде.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have