Abstract
SrTi1−xFexO3−δ ceramics were prepared using a traditional solid-state reaction method. From X-ray diffraction (XRD) result, we found that the doped Fe3+ dissolved in the lattice, and no secondary phase was observed. Cation vacancies in perovskite oxides were identified via positron annihilation lifetime spectroscopy (PALS) measurements. Undoped and Fe-doped SrTiO3 ceramics and single-crystal SrTiO3 were measured by PALS at room temperature. The results show that the main defects in undoped SrTiO3 ceramics are Ti-related defects, and the isolated Ti vacancy lifetime is about 183.4 ps. With the increase of Fe3+, the concentration of the Ti vacancies decreases accompanied by the appearance of the V″Sr − nV o ∙∙ (defect association of Sr vacancies and multiple O vacancies) vacancy defect complexes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.