Study of variation in surface morphology, chemical composition, crystallinity and hardness of laser irradiated silver in dry and wet environments

Abstract

Variation in surface morphology, chemical composition, crystallinity and hardness of laser irradiated silver in dry and wet ambient environments has been investigated. For this purpose, the silver targets were exposed for various number of laser pulses in ambient environment of air, ethanol and de-ionized water for various number of laser pulses i.e. 500, 1000, 1500 and 2000. Scanning Electron Microscope (SEM) was employed to investigate the surface morphology of irradiated silver. SEM analysis reveals significant surface variations for both dry and wet ambient environments. For lower number of pulses, in air environment significant mass removal is observed but in case of ethanol no significant change in surface morphology is observed. In case of de-ionized water small sized cavities are observed with formation of protrusions with spherical top ends. For higher number of laser pulses, refilling of cavities by shock liquefied material, globules and protrusions are observed in case of dry ablation. For ablation in ethanol porous and coarse periodic ripples are observed whereas, for de-ionized water increasing density of protrusions is observed for higher number of pulses. EDS analysis exhibits the variation in chemical composition along with an enhanced diffusion of oxygen under both ambient conditions. The crystal structure of the exposed targets were explored by X-ray Diffraction (XRD) technique. XRD results support the EDS results. Formation of Ag2O in case of air and ethanol whereas, Ag2O and Ag3O in case of de-ionized water confirms the diffusion of oxygen into the silver surface after irradiation. Vickers Hardness tester was employed to measure the hardness of laser treated targets. Enhanced hardness is observed after irradiation in both dry and wet ambient environments. Initial decrease and then increase in hardness is observed with increase in number of laser pulses in air environment. In case of ethanol, increase in number of laser pulses results in continuous decrease in hardness. Whereas, in case of de-ionized water hardness increases with increase in number of laser pulses.