Abstract
The thermally stimulated discharge (TSDC) current is studied for acrylonitrile butadiene rubber (NBR) loaded with different high abrasion furnace carbon black (HAF). TSDC peak appears only for higher HAF contents > 60phr (70 and 80phr of HAF contents), the TSDC spectra consist of a sharp peak corresponding to a peak temperature Tm which is slightly shifted to higher temperature for 70phr loaded NBR samples and to lower temperature for 80phr loaded NBR sample, with poling field (10V/cm to 50V/cm). The activation energy U and relaxation time for TSDC peak were calculated using the initial rise method. The calculated values of U are nearly constant for sample 70phr and slightly increase for sample 80phr with increasing poling field Ep. The calculated values of at peak temperature Tm are nearly constant for two samples (70phr & 80phr) with different poling field, whereas the calculated values of relaxation time at To = 300K increased with increase of poling field.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.