Abstract
An in-depth investigation of the structure, properties, scratch adhesion characteristics of graded Cr-CrN-Cr(1-x)AlxN coatings synthesized onto M42 steel substrates using closed – field unbalanced magnetron sputtering (CFUBMS) was carried out. Advanced microscopy (scanning and transmission electron microscopy), focused ion beam (FIB) imaging, X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and micro–scratch tests was used to investigate the microstructure, mechanical properties and scratch performance as a function of Al content. FIB and TEM investigations revealed that the coatings exhibited a distinct structure; i.e., an adhesive Cr layer, a CrN transition layer and a graded CrAlN top layer with a face centered cubic (FCC) B1 structure. A columnar morphology was exhibited by the coatings and the dimensions of the columnar grains decreased with increasing Al content. Residual stress measurements, obtained from the XRD – sin2ψ method, revealed increasing compressive stresses with increasing Al content. Furthermore, nanoindentation tests showed an increase in mechanical properties, fracture toughness index (H/E) and plastic deformation resistance (H3/E2) as the Al content increased, accompanied by a decrease in the critical load, LC, during scratch testing implying a decrease in scratch toughness.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.