Abstract
A foil of a metastable β Titanium alloy Ti-15V-3Cr-3Sn-3Al was irradiated at the J-PARC neutrino experimental facility with 1.4 × 1020 30 GeV protons at low temperature (100–130 °C at most), and microstructural characterization and hardness testing were conducted as an initial study on the radiation damage effects of Titanium alloy by the high energy proton beam exposure. Expected radiation damage at the beam center is about 0.06–0.12 displacement per atom. A high density (> 1023 m−3) of a nanometer-sized precipitate was observed by TEM studies, which would be identified as martensite α-phase and athermal ω-phase formed during the solution-treatment process to fabricate metastable β alloy. They did not appear to change substantially after irradiation with protons. In the irradiated specimen, we could not identify an obvious signature of radiation damage distributed along the proton beam profile. Very small, nanometer-scale black dots were present at a low density in the most highly irradiated region, and may be small dislocation loops formed during irradiation. The micro-indentation test indicated that the radiation exposure led to tiny increase in Vickers micro-hardness of ΔHV = 20 at beam center. Atom probe tomography reveals compositional fluctuations that reach a maximum amplitude of 10 at% Ti within a space of < 5 nm both before and after irradiation, which may also indicate presence of rich precipitates. These experimental results suggest this specific β alloy may exhibit radiation damage resistance due to the existence of a high density of nano-scale precipitates, but further studies with higher exposure are required to explore this possibility.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.