Abstract
Nanostructure of Y-type hexaferrite with composition of Sr 2 Ni 2 Al x/2 Cr x/2 Fe 12-x O 22 (where x are 0, 0.6, 1.2, 1.8, 2.4 and 3) were prepared by sol–gel auto-combustion method. The influence of Al and Cr doping on the structural and magnetic properties has been investigated. The X-ray diffraction (XRD) patterns confirm phase formation of Y-type hexaferrite. The microstructure and morphology of prepared samples were studied by high resolution field emission scanning electron microscope (FESEM) which shows the hexagonal shape for all of the samples. Magnetic properties were characterized using vibrating sample magnetometer (VSM). The magnetic results revealed that by increasing the Al and Cr to the structure, the coercivity was also increased from 840 Oe to 1160 Oe. Moreover it has been shown that with addition of dopants, saturation magnetization (Ms) and remnant magnetization (Mr) were decreased from 39.61 emu/g to 30.11 emu/g and from 17.51 emu/g to 14.62 emu/g, respectively, due to the entrance of nonmagnetic ions into Fe 3+ sites.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.