Abstract
DSC measurements were performed for Li-Ga alloys of 54 different compositions. The solid compound at the maximum liquidus temperature (739 °C) is observed not at 50 at.% Li (as reported in previous studies) but at 47.1 at.% Li. A eutectic point was detected at 97 at.% Li, in excellent agreement with the result of Thümmel and Klemm and in disagreement with that of Yatsenko et al., Solid compounds were found at 22.1, 33.3, 47.1, 60 and 66.7 at.% Li, of which those at 47.1 and 66.7 at.% Li seem to be accompanied by a non-stoichiometric region. The compound at 22.1 at.% Li corresponds to LiGa 3.42, the existence and structure of which have recently been clarified by Belin.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.