Abstract
In this study, we characterized the optical and electric properties of direct-patternable SnO2 films with embedded Ag nanorods/nanowires prepared by photochemical metal-organic deposition using photosensitive precursors. SnO2 films showed a random orientation of growth independent on the presence of Ag nanorods/nanowires and annealing temperature. The values for sheet resistance and average transmittance of the SnO2 films with and without Ag nanorods/nanowires after annealing at 600°C were 6 kΩ/square and 82.2%, and 418 kΩ/square and 87.2%, respectively. Due to the incorporation of Ag nanorods/nanowires into the SnO2 films, the sheet resistance was remarkably improved, but the optical transmittance was slightly decreased. These results and the direct-patternability of photochemical deposition suggest that SnO2 films with embedded Ag nanorods/nanowires could easily be used in transparent electrodes, eliminating the need for high cost processes such as dry etching.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.