Study of the effects on the Strengthening Mechanism and Wear Behavior of Wear-Resistant Steel of Temperature Controlling in Heat Treatment

Abstract

To improve the wear resistance of the materials used for blades in engineering machinery, this study focused on the microstructural characteristics, mechanical properties, and wear behavior of HB500 grade wear-resistant steel developed using an optimized heat treatment system. To improve the temperature uniformity of the heat treatment furnace, the method of cyclic heating was used to heat the components. Carefully designing the quenching equipment, such as using a cross-shaped press, was employed to enhance the quenching effect and reduce the deformation of the steel plates. The crystal orientation analysis revealed a uniform and fine-grained microstructure, primarily characterized by plate-type tempered martensite, which indicated a good hardenability. The microstructure observations showed that the width of martensite is approximately 200 nm, with a significant presence of dislocations and carbides. Tensile tests and multi-temperature gradient impact tests indicated superior mechanical properties compared to similar grade wear-resistant steels, including a Rockwell hardness of 53, tensile strength of 1610 MPa, yield strength of 1404 MPa, and total elongation around 12.7%. The results of friction and wear experiments indicate that the wear rate decreases as the load increases from 100 N to 300 N, demonstrating an excellent wear resistance under a large load. Observations of the worn surfaces indicated that the wear mainly involved adhesive wear, fatigue wear, and oxidative wear. The properties’ improvements were attributed to microstructure refinement and precipitation strengthening. This study indicates that designing a heat treatment system to control temperature uniformity and stability is feasible.