Abstract
The tensile properties and fracture mechanisms of fully lamellar TiAl based alloy was studied by room and high temperature (400°C) tensile test. The results indicated that: the crack initiated between weak lamellar interfaces．With tension increased, the cracks extended along lamellar direction. Crack propagation resistance was enhanced at colony boundary. Ligaments broke while load increased, and then the main crack and microcrack linked. The fracture process was that the main crack occurred firstly, microcrack appeared and then propagated, the main crack and microcrack were linked，and the alloy fractured finally; The ductility of the alloy at 400°C was superior to that at room temperature; The fracture mechanism of the fully lamellar TiAl based alloy is brittle cleavage fracture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.