Study of ${\rm Nb}_{3}{\rm Al}$ Wires for High-Field Accelerator Magnet Applications

Abstract

Rapid heating, quenching and transformation (RHQT)-processed Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Al wires possess better strain tolerance than Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn wires. However, RHQT-processed Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Al wires so far developed show lower non-copper critical current density (J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> ) than recently developed high-J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn wires in the field range of 12-15 T. Therefore, the development of Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Al wires having enhancing J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> in this field range is a major concern for accelerator magnet designers. Among a number of fabrication parameters that might affect J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> properties, we analysed the effect of thickness of Al and Nb foils in the jelly-roll-shaped filaments embedded in the precursor wires. Mechanical and superconducting properties of these wires with various Al-foil thicknesses in the filaments were investigated.