Abstract
Retained austenite of Q&P (Quenching and Partitioning) processed 0.2C-1.51Si-1.84Mn steel heated in intercritical region and full austenite region are investigated. The results show that the maximum volume fraction of retained austenite heated in intercritical and full austenite region is 13.39% and 5.23% respectively. Carbon partitioning completed within 10 s for both heating modes. The microstructure after full austenitization consisted of martensite laths and thin, inter-lath retained austenite film. Austenite blocks is observed as well after partial austenitization.The distribution of retained austenite is related to the amount of grain boundaries by EBSD techniques.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.