Abstract

During the corrosion of P91 steel in a steam atmosphere of Ar + 80%H 2O, at 650 °C for 100 h the following volatile species were identified by means of a mass spectrometry: Cr(g), CrO 2(g), CrOOH(g), CrO 2(OH) 2(g), Cr(OH) 6(g), FeOOH(g), Fe 0.947O(g), Fe 2O 3(g), CO, CO 2, Mo(g), and HNi(g). Al(g), AlO(g) and FeOOH volatile species were formed on FeAl slurry-coated P91 steel that was oxidized in similar conditions for 200 h. The presence of the volatile species CrO 2(OH) 2(g) during oxidation of the uncoated P91 steel indicated that in these initial stages of oxidation, the sample undergoes a breakdown of chromia scales before the FeAl slurry-coated sample, loosing its protection against oxidation and thus increasing its oxidation rate. In-situ thermogravimetric measurements indicated that the FeAl-slurry coating increased the oxidation resistance of the P91 steel up to 40 times. The morphology/composition and structure of the oxidized samples were also studied using SEM/EDS and XRD techniques.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.