Abstract
Alkaline-earth metal oxide aerogels prepared by sol?gel method followed by autoclave drying are nanocrystalline mesoporous materials with high reactivity. Bulk solid-state reaction of MgO aerogels with CF2Cl2 takes place after a long induction period, during which the active sites are accumulated on the surface of the nanoparticles. It was found that vanadium addition has a promoting effect on this reaction accelerating the process of the active sites formation. A method for characterization of electron-acceptor sites by electron spin resonance spectroscopy using perylene as the spin probe was developed. A good correlation was observed between the rate of the CF2Cl2 destructive sorption and the concentration of weak electron-acceptor sites. Simplified models of such sites were suggested. The acid sites on the modified MgO surface were supposed to be originated from separation of the charged fragments resulting in the surface polarization. Uncompensated oxygen substitution for chlorine and/or fluorine ions leads to appearance of Lewis acid sites while HCl/HF chemisorption results in Bronsted acid sites formation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.