Abstract
Polyaluminocarbosilane(PACS) was synthesized by reaction of polysilocarbonsilane(PSCS) with Al_(AcAc)_3,(AcAc:acetylacetonate) at normal pressure and high temperature,then PACS fibers were prepared through melt spinning of PACS.The composition and structure of PACS fibers were examined by measurements of element analysis,GPC,XPS,IR,()~(29)Si-Solid NMR and()~(27)Al-Solid NMR;the properties of PACS fibers were studied by TG,IR,weight gain and SEM.PACS synthesized through the reaction of Al(AcAc)_3 with PSCS by mass ratio of 6:100 was best fitting for preparing PACS fibers.Its empirical formula was SiC_(2.0)H_(7.5)O_(0.13)Al_(0.018) and the molecular weight was about 1700.The chemical structure unit included SiC_4,SiC_3H etc,and Si—O—Al bonds also existed in the PACS fibers.Under nitrogen atmosphere,the ceramic yield of PACS fibers was about 52%;during the curing process of PACS fibers in air,the Si—H bond reacted with oxygen,and Si—O—Si bond was formed.The ceramic yield of cured PACS fibers was about 80% and the properties of SiC(OAl) and SiC(Al) ceramic fibers were excellent.It was proved that PACS fibers were very fitting for making SiC(OAl) and SiC(Al) ceramic fibers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.