Abstract
Polymeric matrix composite (PMC) has been used in engineering applications instead of metal in the last few years, due to its corrosion resistance and excellent relation between tensile strength/density and elastic modulus/density. However, PMC materials cured by thermal process require high temperature and are time-consuming. The electron beam (EB) curing technology allows its use at room temperature and reduced curing times, and this is one of the main advantages over thermal technology. The aim of this work is to investigate electron beam curable epoxy formulations to use in filament winding processes to produce composite material with similar or better properties than thermal curable composites. The study has been made with commercial epoxy resins and cationic initiators. The epoxy resin samples were irradiated for few minutes with total dose of 150 kGy. The glass transition temperatures ( T g) were determined by dynamic mechanical analyzer (DMA) and the result was 137 °C. The thermal process was carried out in a furnace following three steps: 4 h at 90 °C, increasing temperature from 90 °C to 130 °C during 4 h and 12 h at 130 °C. The total process time was 20 h. The T g of this sample was 102 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call