Abstract
The high crystal quality and low dislocation densities of aluminum nitride (AlN) grown on flat and nano-patterned sapphire substrate that are synthesized by the metal-organic chemical vapor deposition (MOCVD) method are essential for the realization of high-efficiency deep ultraviolet light-emitting diodes. The micro-strains of 0.18 × 10-3 cm-2 for flat substrate AlN and 0.11 × 10-3 cm-2 for nano-patterned substrate AlN are obtained by X-ray diffractometer (XRD). The screw and edge dislocation densities of samples are determined by XRD and transmission electron microscope (TEM), and the results indicate that the nano-patterned substrates are effective in reducing the threading dislocation density. The mechanism of the variation of the threading dislocation in AlN films grown on flat and nano-patterned substrates is investigated comparatively. The etch pit density (EPD) determined by preferential chemical etching is about 1.04 × 108 cm-2 for AlN grown on a nano-patterned substrate, which is slightly smaller than the results obtained by XRD and TEM investigation. Three types of etch pits with different sizes are all revealed on the AlN surface using the hot KOH etching method.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.