Abstract
The aim of this research is to investigate the corrosion behavior of the resistance spot-welded joints of the zinc-coated interstitial free steel (IF steel) in contrast to the steel. For this purpose, the corrosion behavior of the welds and base interstitial-free steel (IF steel) was investigated in two solutions including 0.1 M NaCl + 0.1 M NaOH and 0.1 M NaCl + 0.1 M H2SO4. Potentiodynamic polarization curves and electrochemical impedance spectroscopy test results showed that the corrosion resistance of the base metal and welds in 0.1 M NaCl + 0.1 M NaOH solution is higher than their corrosion resistance in 0.1 M NaCl + 0.1 M H2SO4 solution. It was found that the corrosion resistance of the IF steel base metal in both solutions is higher than that of the welds obtained by the steel. According to the cyclic polarization curves, it can be said that the passive film formed on the specimens in 0.1 M NaCl + 0.1 M NaOH solution is highly susceptible to pitting corrosion while the specimens do not show any passivation behavior in 0.1 M NaCl + 0.1 M H2SO4 solution and undergo severe uniform corrosion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.