Abstract
We studied the CoFeB thickness and composition dependence of tunneling magnetoresistance (TMR) and resistance-area product (RA) in a modified CoFeB/MgO/CoFeB perpendicular magnetic tunnel junction (MTJ), in which the bottom CoFeB is coupled to an in-plane exchange biased magnetic layer. This stack structure allows us to measure TMR and RA of the MTJs in sheet film format without patterning them, using current-in-plane-tunneling (CIPT) technique. The thickness ranges for both top and bottom CoFeB to exhibit perpendicular magnetic anisotropy are similar to what are seen in each single magnetic film stack. However, CIPT measurement revealed that there exists an optimal thickness for both top and bottom CoFeB to achieve the highest TMR value. Magnetic hysteresis loops also suggest the thickness-dependent coupling between the top and bottom CoFeB layers. We studied MTJs with two CoFeB compositions (Co40Fe40B20 and Co20Fe60B20) and found that Co20Fe60B20 MTJs give higher TMR and also wider perpendicular thickness range when used at the top layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.