Abstract
BaTi1-xMnxO3 solid solutions with 0≤x≤0.04 were synthesized in reducing atmosphere (PO2<10-9 Pa) and in air at 1350°C for 2 h. The effect of Mn ions with different valences on the crystal structure of BaTiO3 was studied by the room-temperature Raman scattering, electron spin resonance (ESR) and X-ray powder diffraction analyses. The crystal structure of the solid solution was analyzed to determine the change of its lattice parameters. It was found that in a reducing atmosphere, Mn2+ ions promoted the tetragonal-to-cubic transformation, as both a contraction of c-axis and an extension of a-axis were observed with an increase in Mn content. In contrast, Mn ions in the air-synthesized samples promoted the tetragonal-to-hexagonal transformation. The formation of the hexagonal phase was accompanied by a strong extension of the c-axis of the tetragonal phase from 4.032 Å to 4.042 Å. This was attributed to Jahn-Teller distortions caused by Mn3+ ions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.