AbstractBlends of low‐density polyethylene (LDPE) and poly[ethylene‐co‐(vinyl acetate)] (PEVA), crosslinked by electron‐beam (EB) radiation, formed separate crystalline lattices with a homogeneous amorphous phase. The crystallinity of the EB‐exposed samples slightly decreased, as verified by a slight reduction in the densities and melting heats and temperatures of the samples. The results obtained from both gel content and hot set tests showed that the degree of crosslinking in the amorphous regions was dependent on the dose and blend composition. The molecular weights between the crosslinks, measured from creep data, showed that an increasing PEVA content resulted in tighter network structures, thus supporting the idea that the crosslinking density at a given irradiation dose depends on the amorphous portions of the polymers. Addition of trimethylolpropane trimethacrylate as a radiation sensitizer enhanced the gel content of the neat polyethylene significantly, while the addition of an antioxidant showed the reverse effect. A significant improvement in the tensile strength of the neat PEVA samples was obtained upon EB radiation up to 210 kGy. The irradiated LDPE/PEVA blends showed improved tensile strength and elongation at break when compared to LDPE. Copyright © 2004 Society of Chemical Industry
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.