Abstract
The upcycling process of agricultural waste for cellulose production has been attempted. In this study, cellulose was extracted from sawdust of the rain tree using 4% (w/v) NaOH solution. 1.5 g of extracted cellulose was soaked in water and N,N-dimethylacetamide (DMA) respectively. The soaked cellulose was dissolved in dimethylacetamide/LiCl and reacted with hexamethyldisilazane (HMDS) yielding tetramethylsilylcellulose (TMSC). The IR spectrum shows the presence of-Si (CH3)3 groups: νSi-O at 1047 cm-1, νC-Si at 1252, 843 and 750 cm-1. The 1H-NMR result confirms the presence of-Si (CH3)3 groups at 0 ppm and pyranose ring protons in the range of 2.8-4.5 ppm. SEM image of TMSC shows the fibrous characteristics of cellulose while the EDX shows the presence of Si. The degree of substitution (DS) values calculated from FT-IR and EDX data are 2.33 and 2.08 respectively. 1.0% w/v TMSC solution in THF was prepared. A Small piece (2.0 cm x 4.0 cm) of filter paper was dipped into the TMSC solution for 30 min. The coated paper has an average contact angle of 116o. However the characteristic bands of the TMSC were not observed from FT-IR analysis. While the EDX shows the presence of Si on the paper surface..
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.