Abstract
Ferrate(VI) was prepared by electrooxidation in diaphragm electrolyzer with iron wire gauze as anode and NaOH-KOH mixed solution as electrolyte. The influences of various experimental conditions, such as the volume ratio of NaOH-KOH mixed electrolyte, temperature, current density, passivation of iron anode were investigated on ferrate current efficiency. Due to the low solubility of K2FeO4 in concentrated alkaline solution and the passivation of iron wire gauze anode, a highest current efficiency over 90% was obtained at 45°C and at a current density of 5 mA cm−2 in mixed electrolyte with the volume ratio of NaOH: KOH equal to 6: 4. The result is superior to using NaOH and KOH as electrolyte respectively. In addition, polarization curves, scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS) were employed to further study the effects of synthesis conditions on ferrate(VI) in theory.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.