Abstract
Al 2O3-SiO 2 diphasic gel was synthesized by sol gel route from aluminium nitrate and silicic acid following aqueous phase colloidal interaction. The precursor gel powder was thoroughly characterized by chemical analysis, measurement of surface area and bulk density measurement. The gel powder was further characterized by thermogravimetry, XRD diffraction study of the heat treated samples and Scanning Electron Microscopic (SEM) study of the fractured surfaces of the heat treated compacts. The gel was observed to be a truly di-phasic in nature and was capable of forming nano-structured well distributed mullite phase in the microstructure of the heat treated sample. The gel powder was heated at different temperatures and the formation of Al-O-Si linkage towards the formation of mullite phase (3Al 2O3 , 2SiO 2 ) was studied by Fourier Transform Infra Red (FT-IR) spectroscopy. The characteristic Al-O-Si linkage was found to develop after 600 o C indicating the formation of mullite gel and at 16000 o C the linkage became very strong indicating complete crystallization of mullite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Iranian Journal of Chemistry & Chemical Engineering-international English Edition
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.