Abstract
AbstractThree samples of vinyl ester resins (VERs) were synthesized using bisphenol‐A‐based epoxy resins of varying epoxide equivalent weights (EEW) and acrylic acid in presence of triphenylphosphine as a catalyst at 80 ± 2°C. The cresyl glycidyl ether was used as reactive diluent during the synthesis of VERs. A suitable reaction mechanism was proposed and discussed for the reactions involving epoxide group and acid groups. This was further confirmed by infrared spectroscopic analysis. The maximum peak temperature from DSC were at 106.05°C, 114.20°C, and 128.86°C for benzoyl peroxide initiated VERs viz. samples V1CV, V2CV, and V3CV, respectively, increased with the increase of EEW of the parent epoxy resin. It has also been found that the films of VER having highest EEW of bisphenol‐A epoxy resin showed best chemical resistance amongst all other VERs in this study. The mechanical properties such as hardness and flexibility also showed a similar trend. The thermal stability was found to decrease with the increase of EEW of bisphenol‐A epoxy resin in the VERs. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.