Abstract
The polycrystalline ceramic sample of YFeO3 has been synthesized by high-temperature solid-state reaction method using high-purity oxides. The formation of the compound has been confirmed by the room temperature (RT) X-ray diffraction analysis. The refined lattice parameters obtained by Rietveld analysis are: a = 5.5907 A, b = 7.6082 A and c = 5.2849 A with orthorhombic symmetry in space group Pnma. The average grain size obtained from the SEM micrograph is around 2 µm. The three-dimensional surface morphology has been investigated using atomic force microscopy (AFM), and the average roughness measured in the sampling area of 100.07 µm2 is around 142 nm. The frequency- and temperature-dependent dielectric constant has been measured. The material shows high dielectric constant value (750) at RT. The activation energy obtained from dc conductivity using Arrhenius relation σ = σ oexp(−Ea/kT) is 2.12 eV. Thermal analysis shows phase change around 625 K with minimum weight loss (i.e. 1.27% of initial weight) from RT to 1273 K. The magnetization measurement indicates soft magnetic behaviour.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.