Abstract

The nanopowdery solid solutions of multidoped ceria Ce0.8Nd0.0025Sm0.0025Gd0.005Dy0.095Y0.095O2-δ(x=0.2) with the fluorite type crystal structure of CeO2were synthesized for the first time. Two synthesis procedures were applied: the modified glycine-nitrate procedure (MGNP method) and room temperature self-propagating reaction (SPRT method). All nanopowders were characterized by XRPD analysis, Raman spectroscopy, low temperature nitrogen physisorption, TEM, and SEM methods. According to the XRPD and Raman spectroscopy results, single phase solid solutions of fluorite structure were evidenced regardless of the number of dopants and synthesis procedure. Both XRPD and TEM were analyses evidenced nanometer particle dimensions. The SPRT method results in obtaining sample with higher specific surface area, smaller crystallite and particles sizes, and the same values of the lattice parameter in comparison to pure CeO2. Raman spectroscopy was confirmed to the oxygen vacancies introduced into the ceria lattice when Ce4+ions were replaced with cations (dopants) of lower valence state (3+), which may indicate the potential improvement of ionic conductivity. Additionally, the presence of oxygen vacancies in the lattice ceria, as well as very developed grain boundaries, gives a new possibility for potential application of obtained nanopowders in the area of room temperature ferromagnetism as spintronics.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.