Abstract
Al 2O 3 thin films find a number of applications in optoelectronics, sensors and tribology. In this paper, we report the preparation and characterization of alumina films prepared by both electron beam evaporation and spray pyrolysis method. The electrical properties of alumina films were determined by measuring ( C– V) and ( I– V) characteristics in a metal oxide semiconductor (MOS) structure. A relative dielectric constant ( ε r) of 9.6 for spray pyrolysed films and 8.3 for evaporated films was obtained. The breakdown electric field was found to be around 5 and 1 MV/cm, respectively for spray pyrolysed and evaporated films. The refractive index of alumina films by evaporation was found to be 1.71 and 1.61 at 275 and 500 nm, respectively. The optical band gap of spray pyrolysed films deposited at 300 °C was found to be in the range of 5.40–5.55 eV. Structural, elemental analysis and stoichiometry of the films was studied by scanning electron microscope (SEM), energy dispersive X-ray analysis (EDAX), Auger electron spectroscopy (AES) and Rutherford back scattering (RBS) spectra.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.