Studies on Microstructure and Thermoelectric Properties of p-Type Bi-Sb-Te Based Alloys by Gas Atomization and Hot Extrusion Processes

Abstract

p-Type Bi2Te3 + 75% Sb2Te3 based thermoelectric materials were fabricated via gas atomization and the hot extrusion process. The gas atomized powder showed a clean surface with a spherical shape, and expanded in a wide particle size distribution (average particle size 50 μm). The phase of the fabricated extruded and R-extruded bars was identified using x-ray diffraction. The relative densities of both the extruded and R-extruded samples were measured by Archimedes principle with ∼98% relative density. The R-extruded bar exhibited finer grain microstructure than that of single extrusion process, which was attributed to a recrystallization mechanism during the fabrication. The R-extruded sample showed improved Vickers hardness compared to the extruded sample due to its fine grain microstructure. The electrical conductivity improved for the extruded sample whereas the Seebeck coefficient decreases due to its high carrier concentration. The peak power factor, ∼4.26 × 10−3 w/mK2 was obtained for the single extrusion sample, which is higher than the R-extrusion sample owing to its high electrical properties.