The system SrBi4Ti4−3x Fe4x O15 belonging to bismuth layer structured ferroelectric (BLSF) materials withx = 0, 0.1 and 0.2 has been prepared through solid-state double sintering method. Increase of iron content in SrBi4Ti4O15 resulted in densification of the samples. The normal puckering observed in the sample has been found to decrease and the lattice distortion increased. Dielectric measurements indicate the ferroelectric transition temperature of the samples to be 530°C, 560°C and 606°C. The increase of transition temperature with increasing iron content is correlated with lattice distortion. Conductivity measurements show two slopes and the activation energies have been found to increase with the iron content. Impedance spectroscopy measurements confirm insulating behaviour at lower temperatures. With increase in temperature the samples become conducting and show relaxational effects. The Cole-Cole plots at higher temperatures are found to be semicircles. The relaxation times decrease with the increase of iron content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.