Studies on Chemical Compositions and Water Solubilities of Glasses, (XI)

Abstract

The authors, in continuing the previous studies (This Journal, 59, 61 and 202, 1951) on the relation between chemical compositions and waser solubilities of special glasses containing zirconia in soda-lime-silica glass type (Na2O-CaO-ZrO2-SiO2), reported in the present paper the results of further studies on the water solubility or water resisting degree of various special glass samples containing boric oxide B2O3 in the above mentioned soda-lime-zirconia-silica glass (Na2O-CaO-ZrO2-SiO2-B2O3), in amounts of 2, 4, 6, 8, 10 and 12% by replacing silica, lime or soda.The tests were carried out by the powder method with various heating conditions in water, as following: (1) under the atmospheric pressure on water bath, and (2) under the hydrothermal pressure of superheated steam in the closed autoclave by the following four cases. (a) 8 atm. and about at 172°C, (b) 17 atm. and about at 205°C, (c) 25 atm. and about at 225°C, and (d) 40 atm. and about at 251°C. The results of these experiments, (1) cc of titrated N/50-H2SO4 solution, (2) the percentage of dissolved alkali (AS) by the calculation, (3) the percentage of dissolved alkali and silica as weight decrease (WD), and (4) the percentage of the dissolved alkali to the weight decrease as (AS)/(WD), were odtained and fully discussed. The results were compared with those reported in the previous reports (IX and X) (loc. cit.), and it was determined to be able to obtain the special glass of good water resisting property, which is the special glass type of soda-lime-zirconia borosilicate glass, containing SiO2: 66-68%, ZrO2: 6-8%, B2O3: 10-12%, Na2O: 2-4% and CaO: 3-5%.