Abstract
The empirical formula of average oxide thickness of atomized micron-sized aluminum - magnesium alloy powder was proposed. At the same time, the influence of particle size and the ratio of magnesium on samples’ activity was studied. The phase composition, morphology, and oxidation process of the alloy powders were studied by x-ray diffraction, scanning electron microscope/energy-dispersive x-ray, respectively. Study on the change of powder activity was achieved by standard gas volumn method. The results show that the oxide thickness of the atomized micron-sized aluminum - magnesium alloy powder is positively correlated with the particle size, and the activity decreases with the increase of the particle size and the magnesium content.