Abstract
Highly transparent silicone resin with self-crosslinking structure was prepared using phenyltrimethoxysilane, diphenyldimethoxysilane, 1,3,5,7-cyclotetra(methyl siloxane) and bisvinyltetramethyldisiloxane as main raw materials. The structure of silicone resin was determined by Fourier Transform Infrared Spectroscopy (FT-IR). The light transmittance was measured by UV-Vis spectroscopy. Thermogravimetric analysis (TGA) was used to study the thermal decomposition process. The microstructure of cured self-crosslinking silicone resin is more uniform, resulting in better light transmittance up to 100% in the range of 400nm ~ 800nm. The cured has relatively good heat resistance, the initial thermal decomposition temperature of the cured could be up to 315.8 °C. SEM observations show that the self-crosslinking silicone has a uniform, textured structure, higher transparency compared with the existing condensation silicone material, and can be used as advanced architectural translucent materials and optics packaging materials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.