Abstract
The work presents the results on grains refinement of steel containing 0,45 wt pct carbon resulted from severe plastic deformation (SPD). Different steel structures from prior solutioning and/or thermomechanical treatment were prepared for deformation experimental. A coarse grain ferrite-pearlite structure was achieved applying solutioning. By application of thermomechanical (TM) controlled forging process, performing multistep open die forging, the refined ferrite-pearlite mixture was prepared. Final structure refinement of steel, having different initial structure, was then accomplished applying warm Equal Channel Angular Pressing (ECAP) at 400°C. Employment of this processing route resulted in extensive deformation of ferrite grains and cementite lamellae fragmentation. Applying the highest shear stress (εef - 4) the mixed structure of subgrains and ultrafine grains was present within the ferrite phase. In pearlite grains, modification of cementite lamellae due to shearing, bending, twisting and breaking was found efficient. The coarse cementite lamellae spheroidization was more efficient in prior TM treated steel. The tensile deformation records confirmed strength increase and diversity in strain hardening behaviour.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have